高抗冲，低翘曲PPA Amodel AT-1002 HS美国苏威
Amodel AT-1002 HS
Amodel® AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and better mechanical properties than many unreinforced thermoplastic polyester and nylon resins.
This material was specifically designed for automotive electrical/electronic applications such as connectors, sockets and sensors.
Natural: AT-1002 HS NT
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 密度 | 1.13 | -- | g/cm³ | ISO 1183/A |
| 收缩率 | ASTM D955 | |||
| 流动 | 2.0 | -- | % | ASTM D955 |
| 横向流动 | 2.1 | -- | % | ASTM D955 |
| 吸水率 (24 hr) | 0.50 | -- | % | ASTM D570 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 拉伸模量 | ||||
| -- | 2760 | 2760 | MPa | ASTM D638 |
| 23°C | 2760 | -- | MPa | ISO 527-2 |
| 100°C | 2100 | -- | MPa | ISO 527-2 |
| 拉伸应力 | ||||
| 屈服, 23°C | 75.2 | -- | MPa | ISO 527-2 |
| 屈服, 100°C | 38.6 | -- | MPa | ISO 527-2 |
| 断裂, 23°C | 68.3 | -- | MPa | ISO 527-2 |
| -- | 83.4 | 76.5 | MPa | ASTM D638 |
| 拉伸应变 | ||||
| 屈服, 23°C | 5.0 | -- | % | ISO 527-2 |
| 屈服, 100°C | 3.7 | -- | % | ISO 527-2 |
| 断裂 1 | 80 | 100 | % | ASTM D638 |
| 断裂, 23°C | 15 | -- | % | ISO 527-2 |
| 弯曲模量 | ||||
| -- | 2210 | 2280 | MPa | ASTM D790 |
| 23°C | 2280 | -- | MPa | ISO 178 |
| 100°C | 1720 | -- | MPa | ISO 178 |
| 弯曲强度 | ||||
| -- | 103 | 73.1 | MPa | ASTM D790 |
| 23°C | 79.3 | -- | MPa | ISO 178 |
| 100°C | 49.6 | -- | MPa | ISO 178 |
| 剪切强度 | 64.1 | 57.2 | MPa | ASTM D732 |